Fine details, smooth surface finish, watertight. Ideal for validating product appearance, non-functional prototypes with intricate details, figures & miniatures. The mechanical properties of the standard resin are weaker than ABS or PETG's. Choose Tough Resin for applications that require higher strength. Not suitable for high temperature (greater than 40 °C/106 °F) environment. Printed with SLA technology.
-
Properties
-
Capabilities
Average Lead Time: 3 business days
Layer Height: 100 μm
Dimensional Accuracy: ± 0.1% with a lower limit of ± 0.025 mm (± 0.0009″)
Available Types&Colors
-
Standard Resin
-
Tough Resin
-
Clear Resin
Technical Data Sheet
Standard Resin (SLA) | |||
---|---|---|---|
Mechanical Properties | |||
Test Method | Property Description | Metric | Imperial |
D638M | Tensile Strength at Break | 33.8 - 40.2 MPa | 4.9 - 5.8 ksi |
D638M | Tensile Modulus | 2,370 - 2,650 MPa | 344 - 384 ksi |
D638M | Elongation at Break | 6 - 9% | 6 - 9% |
D790M | Flexural Strength | 66.8 - 67.8 MPa | 9.7 - 9.8 ksi |
D790M | Flexural Modulus | 2,178 - 2,222 MPa | 315 - 322 ksi |
D256A | Impact Strength (notched Izod) | 23 - 29 J/cm | 0.43 - 0.54 ft-lb/in |
D2240 | Hardness (Shore D) | 79 | 79 |
D570-98 | Water Absorption | 0.40% | 0.40% |
Thermal Properties | |||
Test Method | Property Description | Metric | Imperial |
E1545-00 | Tg | 41 - 43°C | 111°F |
D648 | Heat deflection temperature (@ 0.46 MPa, 66 psi) | 46°C | 115°F |
D648 | Heat deflection temperature (@ 1.81 MPa, 264 psi) | 41°C | 105°F |
Tough Resin (SLA) | |||
---|---|---|---|
Mechanical Properties | |||
Test Method | Property Description | Metric | Imperial |
D638-14 | Tensile Strength at Yield | 46.9 MPa | 6.8 ksi |
D638-14 | Tensile Modulus | 2,310 MPa | 335 ksi |
D638M | Elongation at Break | 24% | 24% |
D790M | Flexural Strength | 73.8 MPa | 10.7 ksi |
D790M | Flexural Modulus | 2,054 MPa | 298 ksi |
D256A | Impact Strength (notched Izod) | 47.5 J/m | 0.89 ft-lb/in |
D2240 | Hardness (Shore D) | 83 | 83 |
D570-98 | Water Absorption | 0.75% | 0.75% |
Thermal Properties | |||
Test Method | Property Description | Metric | Imperial |
D3418-15 | Glass Transition Temperature (DSC) | 53°C | 127°F |
D648 | Heat deflection temperature (@ 0.46 MPa, 66 psi) | 62°C | 144°F |
D648 | Heat deflection temperature (@ 1.81 MPa, 264 psi) | 50°C | 122°F |